Lattice location of Mg in GaN: a fresh look at doping limitations

Radioactive ^{27}Mg (t_{1/2}=9.5  min) was implanted into GaN of different doping types at CERN's ISOLDE facility and its lattice site determined via β^{-} emission channeling. Following implantations between room temperature and 800 °C, the majority of ^{27}Mg occupies the substitutional Ga sites; however, below 350 °C significant fractions were also found on interstitial positions ∼0.6  Å from ideal octahedral sites. The interstitial fraction of Mg was correlated with the GaN doping character, being highest (up to 31%) in samples doped p type with 2×10^{19}  cm^{-3} stable Mg during epilayer growth, and lowest in Si-doped n-GaN, thus giving direct evidence for the amphoteric character of Mg. Implanting above 350 °C converts interstitial ^{27}Mg to substitutional Ga sites, which allows estimating the activation energy for migration of interstitial Mg as between 1.3 and 2.0 eV.

Publication year:2017

BOF-keylabel:yes

IOF-keylabel:yes

BOF-publication weight:6

CSS-citation score:2

Authors:International

Authors from:Higher Education

Accessibility:Open