Temperature Dependence of Thermophysical Properties of Carbon/Polyamide Composite
Boekbijdrage - Boekhoofdstuk Conferentiebijdrage
In this study, the temperature dependence of heat capacity, thermal expansion, density, and thermal conductivity of carbon/polyamide composites has been studied. Results showed that the specific heat capacity of the C/PA composite increases with temperature, and major transitions have been observed at glass transition (Tg) and melting (Tm) temperatures. Due to the presence of fibers, the CTE values in the fiber direction of C/PA samples were smaller by an order of magnitude than in the transverse direction. The density measurement results showed that with an increase in temperature, volume increases, so density decreases. The laser flash technique has been used to measure the heat diffusivity of the C/PA composite, which is then used to calculate thermal conductivity. Results showed that the average thermal conductivity increases with temperature along the fiber direction and increases with a small rate in the beginning and is almost uniformly distributed later, in the transverse direction.
Boek: Proceedings of the 20th European Conference on Composite Materials Vol 3 – Characterization
Pagina's: 224 - 231
Aantal pagina's: 1196
ISBN:978-2-9701614-0-0
Jaar van publicatie:2022
Toegankelijkheid:Open
- Zie ook: Cooling rate effects on consolidation quality of carbon fibre reinforced polyamide6 (CF/PA6) laminated composites
- Zie ook: TENSILE FATIGUE PERFORMANCE OF CARBON-CARBON HYBRID QUASIISOTROPIC LAMINATE
- Zie ook: Bond strength analysis in continuous fiber reinforced thermoplastics
- Zie ook: Macroscale Magnetic Alignment of Multiple Discontinuous Ferromagnetic Fibres in a Polymer Matrix
- Zie ook: Predicting the effective thermal conductivity of injection moulded short glass fibre reinforced polyamide using different effective medium theories
- Zie ook: Generation of realistic 2D transverse microstructures of unidirectional fiber-reinforced composites using a Generative Adversarial Network
- Zie ook: Cooling rate effects on consolidation quality of carbon fibre reinforced polyamide6 (CF/PA6) laminated composites
- Zie ook: CRYSTALLINITY PREDICTION OF SHORT CARBON FIBRE REINFORCED POLYAMIDE 6 COMPOSITES MANUFACTURED BY FUSED FILAMENT FABRICATION