Microscopic investigation of as built and hot isostatic pressed Hastelloy X processed by Selective Laser Melting

Microstructural characteristics of Hastelloy X produced by Selective Laser Melting have been investigated by various microscopic techniques in the as built (AB) condition and after hot isostatic pressing (HIP). At sub-grain level the AB material consists of columnar high density dislocation cells while the HIP sample consists of columnar sub-grains with lower dislocation density that originate from the original dislocation cells, contradicting existing models. The sub-grains contain nanoscale precipitates enriched in Al, Ti, Cr and O, located at sub-grain boundaries in the AB condition and within the grains after HIP. At some grain boundaries, micrometer sized chromium carbides are detected after HIP. Micro hardness within the grains was found to decrease after HIP, which was attributed to the decrease in dislocation density due to recovery annealing.

Jaar van publicatie:2019

Trefwoorden:A1 Journal article

BOF-keylabel:ja

BOF-publication weight:1

CSS-citation score:2

Authors from:Higher Education

Toegankelijkheid:Open