Nucleation and growth mechanisms of Al2O3 atomic layer deposition on synthetic polycrystalline MoS2

Two-dimensional (2D) semiconducting transition metal dichalcogenides (TMDs) are of great interest for applications in nano-electronic devices. Their incorporation requires the deposition of nm-thin and continuous high-k dielectric layers on the 2D TMDs. Atomic layer deposition (ALD) of high-k dielectric layers is well established on Si surfaces: the importance of a high nucleation density for rapid layer closure is well known and the nucleation mechanisms have been thoroughly investigated. In contrast, the nucleation of ALD on 2D TMD surfaces is less well understood and a quantitative analysis of the deposition process is lacking. Therefore, in this work, we investigate the growth of Al2O3 (using Al(CH3)3/H2O ALD) on MoS2 whereby we attempt to provide a complete insight into the use of several complementary characterization techniques, including X-ray photo-electron spectroscopy, elastic recoil detection analysis, scanning electron microscopy, and time-of-flight secondary ion mass spectrometry. To reveal the inherent reactivity of MoS2, we exclude the impact of surface contamination from a transfer process by direct Al2O3 deposition on synthetic MoS2 layers obtained by a high temperature sulfurization process. It is shown that Al2O3 ALD on the MoS2 surface is strongly inhibited at temperatures between 125°C and 300°C, with no growth occurring on MoS2 crystal basal planes and selective nucleation only at line defects or grain boundaries at MoS2 top surface. During further deposition, the as-formed Al2O3 nano-ribbons grow in both vertical and lateral directions. Eventually, a continuous Al2O3 film is obtained by lateral growth over the MoS2 crystal basal plane, with the point of layer closure determined by the grain size at the MoS2 top surface and the lateral growth rate. The created Al2O3/MoS2 interface consists mainly of van der Waals interactions. The nucleation is improved by contributions of reversible adsorption on the MoS2 basal planes by using low deposition temperature in combination with short purge times. While this results in a more two-dimensional growth, additional H and C impurities are incorporated in the Al2O3 layers. To conclude, our growth study reveals that the inherent reactivity of the MoS2 basal plane for ALD is extremely low, and this confirms the need for functionalization methods of the TMD surface to enable ALD nucleation.

Jaar van publicatie:2017

BOF-keylabel:ja

IOF-keylabel:ja

BOF-publication weight:1

CSS-citation score:2

Authors from:Government, Higher Education

Toegankelijkheid:Open