Effect of conditioning and 1 year aging on the bond strength and interfacial morphology of glass-ionomer cement bonded to dentin

Journal Contribution - Journal Article

OBJECTIVE: The purpose of this study was to determine the bond stability and the change in interfacial ultra-structure of a conventional glass-ionomer cement bonded to dentin, with and without pre-treatment using a polyalkenoic acid conditioner. METHODS: The occlusal dentin surfaces of six teeth were ground flat. Glass-ionomer cement was bonded to the surfaces either with or without polyalkenoic acid conditioning. The teeth were sectioned into 1-mm2 stick-shaped specimens. The specimens obtained were randomly assigned to two groups with different periods of storage in water: 1 week and 1 year. The micro-tensile bond strength (μTBS) was determined for each storage time. Additional specimens were prepared for Transmission Electron Microscopy (TEM); they were produced with or without prior polyalkenoic acid conditioning in the same way as in the μTBS test. RESULTS: There was no significant difference in μTBS to conditioned dentin and non-conditioned dentin (p > 0.05). The failures appeared to be of a mixed nature, although aging caused more areas of cohesive than adhesive failure in both groups. The TEM observation showed an intermediate layer, a matrix-rich layer and a partially demineralized layer in the polyalkenoic acid conditioned group. SIGNIFICANCE: Aging did not reduce the bond strength of the conventional glass-ionomer cement to dentin with or without the use of a polyalkenoic acid conditioner.
Journal: Dental Materials
ISSN: 0109-5641
Issue: 1
Volume: 37
Pages: 106 - 112
Publication year:2021
BOF-keylabel:yes
IOF-keylabel:yes
BOF-publication weight:6
CSS-citation score:2
Authors:International
Authors from:Higher Education
Accessibility:Open