Byproduct-based ettringite binder - A synergy between ladle slag and gypsum

© 2018 Elsevier Ltd Ladle slag (LS) is a byproduct from the steel industry that is usually reactive on its own and hydrates towards cementitious phases when mixed with water. However, these reaction products are often metastable, leading to micro-structural changes between 7 and 30 days after mixing. To address this issue, in this experimental investigation, a new binder was designed where LS was mixed with gypsum in order to deliver an ettringite-based binder (LSG). The experimental results revealed that the dominant crystalline phase of LSG was ettringite, which remained stable with no conversion at later stages. For better understanding of the ettringite-based binder, mortar characterization, mechanical properties, and durability of LSG were investigated. LSG showed good mechanical properties and excellent freeze-thaw resistance after 300 cycles, which is comparable to other calcium sulfoaluminate cements. Therefore, as a result, the byproduct-based ettringite binder synthesized herein could offer a solution to steelmaking byproducts with a low-CO 2 binder, which could be used in a wide range of applications in the construction industry.

Publication year:2019

BOF-keylabel:yes

IOF-keylabel:yes

BOF-publication weight:3

CSS-citation score:2

Authors:International

Authors from:Higher Education

Accessibility:Closed