Ti surface doping of $LiNi_{0.5}Mn_{1.5}O_{4-\delta}$ positive electrodes for lithium ion batteries

The particle surface of LiNi0.5Mn1.5O4−δ (LNMO), a Li-ion battery cathode material, has been modified by Ti cation doping through a hydrolysiscondensation reaction followed by annealing in oxygen. The effect of different annealing temperatures (500850 °C) on the Ti distribution and electrochemical performance of the surface modified LNMO was investigated. Ti cations diffuse from the preformed amorphous TiOx layer into the LNMO surface during annealing at 500 °C. This results in a 24 nm thick Ti-rich spinel surface having lower Mn and Ni content compared to the core of the LNMO particles, which was observed with scanning transmission electron microscopy coupled with compositional EDX mapping. An increase in the annealing temperature promotes the formation of a Ti bulk doped LiNi(0.5−w)Mn(1.5+w)−tTitO4 phase and Ti-rich LiNi0.5Mn1.5−yTiyO4 segregates above 750 °C. Fourier-transform infrared spectrometry indicates increasing NiMn ordering with annealing temperature, for both bare and surface modified LNMO. Ti surface modified LNMO annealed at 500 °C shows a superior cyclic stability, coulombic efficiency and rate performance compared to bare LNMO annealed at 500 °C when cycled at 3.44.9 V vs. Li/Li+. The improvements are probably due to suppressed Ni and Mn dissolution with Ti surface doping.

Publication year:2018

Keywords:A1 Journal article

BOF-keylabel:yes

BOF-publication weight:1

CSS-citation score:1

Authors:International

Authors from:Higher Education

Accessibility:Open